Uns S32205 Uns S31803 F55 1.4462 Duplex Stainless Steel
Feb 18, 2017
Basic Info
  • Model NO.: UNS S32205 UNS S31803 F55 1.4462 2205

  • Standard: ASTM, EN

  • Certification: ISO, SGS

  • Technique: Hot Rolled

  • Size Range: Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm

  • Delivery Condition: Hot Rolled, Forged, Annealed, Quenched and Tempered

  • Type: Stainless Steel Bars

  • Grade: 200 Series

  • Shape: Round

  • Surface Treatment: Bright

  • Similar Grade: Uns S32205 Uns S31803 F55 1.4462 2205

  • MOQ: 500kgs

  • Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm

  • HS Code: 7228600000

  • Quality Standard

ASTM A182 Standard Specification for Forged or Rolled Alloy-Steel Pipe Flanges, Forged Fittings, and Valves and Parts
ASTM A276 Standard Specification for Stainless Steel Bars and Shapes
EN 10088 part3 stainless steel
ASTM A240 Standard Specification for Chromium and Chromium Nickel Stainless Steel Plate Sheet and Strip
Similar Grades
 

ASTM A240
EN10088AFNOR
UNS S32205/S318031.4462 X2CrNiMoN 22.5.3Z3 CrNi 22.05 AZ

Chemical Composition(%)
 

Steel Grade
CSiMnPSCrNiMoN
22050.03 max1.0 max2.0 max0.030 max0.020 max22.0-23.04.50-6.503.0-3.50.14-0.20
1.44620.03 max1.0 max2.0 max0.035 max0.015 max21.0-23.04.50-6.502.50-5.500.10-0.22

Mechanical Properties (Annealed)
 

Hardness (HB)
Tensile Strength (Mpa)Yield Strength (Mpa)Elongation (%) (Long.)Impact Value (J) (Long.)
270 max650-880450 min25 min100 min

Corrosion Resistance
General Corrosion: Because of its high chromium (22%), molybdenum (3%), and nitrogen (0.18%) contents, the corrosion resistance properties of 2205 duplex stainless steel are superior to that of 316L or 317L in most environments.
Localized Corrosion Resistance: The chromium, molybdenum, and nitrogen in 2205 duplex stainless steel also provide excellent resistance to pitting and crevice corrosion even in very oxidizing and acidic solutions.
Stress Corrosion Resistance: The duplex microstructure is known to improve the stress corrosion cracking resistance of stainless steels.
Chloride stress corrosion cracking of austenitic stainless steels can occur when the necessary conditions of temperature, tensile stress, oxygen, and chlorides are present. Since these conditions are not easily controlled, stress corrosion cracking has often been a barrier to utilizing 304L, 316L, or 317L.
Corrosion Fatigue Resistence: 2205 duplex stainless steel combines high strength and high corrosion resistance to produce high corrosion fatigue strength. Applications in which processing equipment is subject to both an aggresively corrosive enviroment and to cycle loading can benefit from the properties of 2205 duplex stainless steel.
Processing
Cold Forming: 2205 duplex stainless steel is readily sheared and cold formed on equipment suited to working stainless steels. However, because of the high strength and rapid work hardening of 2205 duplex stainless steel, forces substantially higher than those for austenitic steels are required to cold form it. Also because of the high strength, a somewhat larger allowance must be made for springback.
Heat Treatment:2205 duplex stainless steel should be annealed at 1900°F minimum, followed by rapid cooling, ideally by water quenching. This treatment applies to both solution annealing and stress relieving. Stress relief treatments at any lower temperature carry the risk of precipitation of detrimental intermetallic or nonmetallic phases.
Structure

 